Simulation of skyrmionic structure in synthetic antiferrromagnet about workshop

[marijanbeg]

Hi @gaurav123shukla, we do not have a tutorial on this topic, but all the necessary ingredients should be there (exchange, RKKY, etc.) I suggest you just try to do it starting from those tutorials.

Regarding initial magnetisation, you need to set it in all subregions of your sample. If you expect to get a skyrmion, then initialising the system with something which looks like a skyrmion should be sufficient.

[gaurav123shukla]

Yes sir; I took help from rkky interraction file. But sir when I run the oommf ,some error ocuured. Sir I have also started docker but same error is showing. Sir i am sending ipynb file for same, please check sir it whether it is running in yor machine or not,so that i would know where I am making mistake.
Ta_CFA_MgO.zip