ValueError: Could not find fermi within low concentration about amset

[utf]

I have never heard of carrier concentrations that low before. For GaAs you typically see concentrations from 1e13 and above.

Could there be a mistake with your units? The concentration should be in cm^-3.

[thienbinh92]

I thought about a low doping concentration because if I set the doping concentration of -3e13, the obtained average electronic conductivity is very much higher compared with the experimental one (1e-6 to 1e-8 /ohm cm). I got information from GaAs: "Intrinsic Carrier Concentration | 1.79 x 106 cm-3". I also found a higher doping concentration in another document (1e13~1e14), but don't know the reasonable one. Maybe a range of doping concentrations is needed. Is the accuracy of electronic conductivity reasonable?

  Average conductivity (σ), Seebeck (S) and mobility (μ) results:

    conc [cm-3]    temp [K]    σ [S/m]    S [µV/K]    μ [cm2/Vs]
  -------------  ----------  ---------  ----------  ------------
      -3.00e+13       201.0   1.72e+01   -8.56e+02       35825.3
      -3.00e+13       290.0   7.78e+00   -9.11e+02       16187.2
      -3.00e+13       401.0   4.18e+00   -9.67e+02        8705.5
      -3.00e+13       506.0   2.81e+00   -1.01e+03        5836.5
      -3.00e+13       605.0   2.81e+00   -9.84e+02        4387.0
      -3.00e+13       789.0   3.10e+01   -7.11e+02        2906.5
      -3.00e+13       994.0   2.40e+02   -5.45e+02        1989.5